Kivonat az ISO 683-13 : 1986 szabványból
Acélfajta 2 | Kémiai összetevők tömegszázalék %1 | ||||||||||||||
C max. | Si max. | Mn max. | P max. | S max. | N | Al | Cr | Mo | Nb3) | Ni | Se min. | Ti | Cu | Az acélcsoport jelzése4 | |
Ferrites acél | |||||||||||||||
8 | 0,08 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 16,0 - 18,0 | – | – | 1,0 max. | – | – | – | F1 |
8b | 0,07 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 16,0 - 18,0 | – | – | 1,0 max. | – | 7 x % C≤1,10 | – | F1 |
9c | 0,08 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 16,0 - 18,0 | 0,90 - 1,30 | – | 1,0 - max. | – | – | – | F1 |
F1 | 0,025 | 1,0 | 1,0 | 0,040 | 0,030 | 0,025 max | – | 17,0 - 19,0 | 1,75 - 2,50 | –6 | 0,60 max. | – | –6 | – | F1 |
Martenzites acél | |||||||||||||||
3 | 0,09-0,15 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 11,5 - 13,5 | – | – | 1,0 max. | – | – | – | C1 |
7 | 0,08-0,15 | 1,0 | 1,5 | 0,060 | 0,15 - 0,35 | – | – | 12,0 - 14,0 | 0,60 max7 | – | 1,0 max. | – | – | – | C4 |
4 | 0,16-0,25 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 12,0 - 14,0 | – | – | 1,0 max. | – | – | – | C1 |
9a | 0,10-0,17 | 1,0 | 1,5 | 0,060 | 0,15 - 0,35 | – | – | 15,5 - 17,5 | 0,60 max7 | – | 1,0 max. | – | – | – | C3 |
9b | 0,14-0,23 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 15,0 - 17,5 | – | – | 1,5 - 2,5 | – | – | – | C3 |
5 | 0,26-0,35 | 1,0 | 1,0 | 0,040 | 0,030 | – | – | 12,0 - 14,0 | – | – | 1,0 max. | – | – | – | C1 |
Ausztenites acél | |||||||||||||||
10 | 0,03 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 17,0 - 19,0 | – | – | 9,0 - 12,0 | – | – | – | A28 |
11 | 0,07 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 17,0 - 19,0 | – | – | 8,0 - 11,0 | – | – | – | A2 |
15 | 0,08 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 17,0 - 19,0 | – | 9,0 - 12,0 | – | 5 x %≤0,80 | – | A39 | |
16 | 0,08 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 17,0 - 19,0 | – | 10 x % C≤1,0 | 9,0 - 12,0 | – | – | – | A39 |
17 | 0,12 | 1,0 | 2,0 | 0,060 | 0,15 - 0,35 | – | – | 17,0 - 19,0 | –10) | – | 8,0 - 10,011 | – | – | – | A1 |
13 | 0,10 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 17,0 - 19,0 | – | – | 11,0 - 13,0 | – | – | – | A2 |
19 | 0,03 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 16,5 - 18,5 | 2,0 - 2,5 | – | 11,0 - 14,0 | – | – | – | A4 |
20 | 0,07 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 16,5 - 18,5 | 2,0 - 2,5 | – | 10,5 - 13,5 | – | – | – | A4 |
21 | 0,08 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 16,5 - 18,5 | 2,0 - 2,5 | – | 11,0-14,0 | – | 5 x %≤0,80 | – | A59 |
23 | 0,08 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 16,5 - 18,5 | 2,0 - 2,5 | 10 x % C≤1,0 | 11,0 - 14,0 | – | – | – | A59 |
19a | 0,03 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 16,5 - 18,5 | 2,5 - 3,0 | – | 11,5 - 14,5 | – | – | – | A4 |
20a | 0,07 | 1,0 | 2,0 | 0,045 | 0,030 | – | – | 16,5 - 18,5 | 2,5 - 3,0 | – | 11,0 - 14,0 | – | – | – | A4 |
10N | 0,03 | 1,0 | 2,0 | 0,045 | 0,030 | 0,12 - 0,22 | – | 17,0-19,0 | – | – | 8,5 - 11,5 | – | – | – | A2 |
19N | 0,03 | 1,0 | 2,0 | 0,045 | 0,030 | 0,12 - 0,22 | – | 16,5 - 18,5 | 2,0 - 2,5 | – | 10,5 - 13,5 | – | – | – | A48 |
19aN | 0,03 | 1,0 | 2,0 | 0,045 | 0,030 | 0,12 - 0,22 | – | 16,5 - 18,5 | 2,5 - 3,0 | – | 11,5 - 14,5 | – | – | – | A48 |
- A táblázatban nem lett minden lehetséges ötvözőelem számszerűen felsorolva, amennyiben a technológia megkívánja, a megrendelő hozzájárulásával egyéb ötvözők felhasználása is megengedett. Törekedni kell arra, hogy más elemek, amelyek selejtből vagy más gyártás során használt nyersanyagból származnak ne keveredjenek az acélhoz, mert ezek a szennyeződések az edzhetőség, a mechanikai tulajdonságok, és a használhatóság rovására mehetnek.
- Ezek a számok csak előzetesen kalkulált értékek. Még nincsenek nemzetközi normák meghatározva.
- A tantál mennyisége határozza meg a nióbium szintet.
- Ezt nem tartalmazza az ISO 683 : 1986 szabvány.
- (C+N) tömegaránya max. 0,040 %
- 8 x (C+N) kisebb vagy egyenlő (Nb+Ti) kisebb vagy egyenlő, mint 0,80 % tömegarány.
- A megegyezés utáni ajánlatkérések és rendelések időpontjánál az acél a molibdén-tartalom 0,20 % és 0,60 % (m/m) között változhat.
- Kitűnően ellenáll szemcseközi korróziónak.
- Stabilizált acél
- A gyártó szabadon megválaszthatja a molibdén mennyiségét 0,70 % tömegarányig.
- Varratnélküli csövek alapanyagánál a maximális nikkel tartalmat 0,5 % tömegarányig lehet megemelni.